The dielectric tunable Ba0.6Sr0.4TiO3-Ba4Ti13O30 (BST-BT4/13) composite ceramics with high dielectric phase contents and good temperature stability have been prepared by the solidstate reaction method. The effects of Ba4Ti13O30contents and sintering temperatures on the microstructure, dielectric and tuning properties were investigated. Results show that the increase of BT4/13 content is beneficial to the improvement of sintering properties, the decrease of dielectric constant and the enhancement of temperature stability of BST-BT4/13 composite ceramics, but it will reduce the tuning rate of BST-BT4/13 composite ceramics. With the increase of sintering temperature, the dielectric constant of BST-BT4/13 composite ceramics increases. As the volume fraction of BT4/13 phase reaches as high as 92%, the BST-BT4/13 composite ceramics have excellent temperature stability at 20~160 ℃ and its dielectric constant maintains almost unchanged at 20~65 ℃, and still exhibits obvious dielectric nonlinearity with the tunability of 1% at a DC bias field strength of 10 kV/cm.
参考文献
相似文献
引证文献
引用本文
郑瑞,金灯仁,徐凯,程晋荣. BST-BT4/13复合陶瓷介电调谐性能的研究[J].压电与声光,2019,41(1):12-16. ZHENG Rui, JIN Dengren, XU Kai, CHENG Jinrong. Study on Dielectric Tunable Properties of BST-BT4/13 Composite Ceramics[J]. PIEZOELECTRICS AND ACOUSTOOPTICS